Densification of Nanocrystalline Yttria by Low Temperature Spark Plasma Sintering

We investigated the densification of undoped, nanocrystalline yttria (Y 2 O 3 ) powder by spark plasma sintering (SPS) at sintering temperatures between 650°C and 1050°C at a heating rate of 10°C/min and an applied stress of 83 MPa. In spite of the low sinterability of the undoped Y 2 O 3 , a remarkable densification of the powder started at about 600°C, and a theoretical density of more than 97% was achieved at a sintering temperature of 850°C with a grain size of about 500 nm. The low temperature SPS is effective for fabricating dense Y 2 O 3 polycrystals.