Photostimulated discharge in electret polymers: an alternative approach for investigating deep traps

The stability of space charge in electrets such as polytetrafluoroethylene (PTFE), polyethylene terephthalate (PETP) and polypropylene (PP) under ultraviolet irradiation has been investigated using photostimulated discharge spectroscopy. While only weak discharge currents were observed in PTFE coated with semitransparent gold electrodes, up to 15 pA/cm/sup 2/ were found in PETP around the UV absorption edge near 310 nm. Space charge profiles obtained with the piezoelectrically generated pressure step method indicate that near-surface charges were almost completely removed. In PP foam, recent findings of a UV-reduced d/sub 33/ coefficient were confirmed for exposure times of up to 3.5 h, and a discharge peak at 200 nm could be assigned to the charges stored on the surfaces of the voids. The unique morphology and the (quasi-)piezoelectric properties of cellular PP make it a role model for the future investigation of charge storage in electrets.