Self-organization in complex oxide thin films: from 2D to 0D nanostructures of SrRuO₃and CoCr₂O₄

We report here on the controlled fabrication of nanostructures of varied dimensionality by self-organization processes in the heteroepitaxial growth of SrRuO3 (SRO) and CoCr2O4 (CCO) films. The surface of SRO films on SrTiO3(001) substrates can show extremely smooth terraces (2D objects) separated by atomic steps, a structure of faceted islands (0D objects), a cross-hatch morphology (1D objects), an array of finger-like units (1D objects), or an array of giant bunched steps (1D objects). The surface can be tailored to a particular structure by controlling the vicinality of the substrate and the growth rate and nominal thickness of the film. In the case of CCO films, grown on (001)-oriented MgAl2O4 or MgO substrates, high aspect ratio {111}-faceted pyramids and hut clusters (0D objects), highly oriented and having a similar size, appear above a critical thickness. The size and spatial density can be tuned by varying deposition temperature, nominal thickness, and substrate. This dependence allows the fabrication of surfaces being fully faceted (2D objects), or having arrays of dislocated pyramids of up to micrometric size, or small coherently lattice strained pyramids having a nanometric size. We discuss the driving forces that originate the peculiar SRO and CCO nanostructures. The findings illustrate that the growth of complex oxides can promote a variety of novel self-organized morphologies, and suggest original strategies to fabricate templates or hybrid structures of oxides combining varied functionalities.