340 nm‐band high‐power InAlGaN quantum well ultraviolet light‐emitting diode using p‐type InAlGaN layers

In order to achieve high‐efficiency ultraviolet (UV) light‐emitting diodes (LEDs), p‐type layers with sufficient hole concentration is quite important to suppress the electron overflow. We introduced Mg‐doped InAlGaN for p‐type layers of the UV‐LEDs for the purpose of obtaining higher hole concentration, and achieved high power CW operations of the UV‐LEDs. 340 nm‐band InAlGaN‐based multi‐quantum‐well (MQWs) UV‐LEDs with Mg‐doped InAlGaN electron‐blocking layer (EBL) and Mg‐doped InAlGaN layers were grown on sapphire substrates by metal‐organic chemical vapor deposition (MOCVD). The output power of UV‐LED with p‐InAlGaN layers was approximately 4.7 times larger than that with p‐AlGaN layers. Maximum output power and the external quantum efficiency (EQE) of the LED with p‐InAlGaN layers were 8.4 mW and 0.9%, respectively, at emission wavelength of 346 nm under room temperature (RT) CW operation. From these results, p‐InAlGaN is shown to be useful for the realization of high‐efficiency UV‐LEDs. (© 2008 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)