Cryogenic relaxations of polystyrene and poly(fluorinated styrenes)

The effect of structural and morphologic modifications of styrene and fluorinated styrene polymers on their internal friction was studied by means of a free‐oscillating torsional pendulum at temperatures from 300° to 4.2°K and frequencies of 1 to 2 Hz. Atactic and isotactic polystyrene gave the previously observed δ and β′ loss peaks at 38° and 100°K, respectively. These losses decrease in intensity with crystallinity in isotactic polystyrene but remain relatively unchanged in uniaxially drawn atactic polymer. Atactic polypentafluorostyrene showed an intense δ loss peak at 52°K and a broad shoulder around 100°K, which extends toward the β′ relaxation. In poly‐α,β,β‐trifluorostyrene, the δ loss peak is largely suppressed, the logarithmic decrement showing only broad maxima at 22° and 100°K. Plasticization of atactic polystyrene with 2% mineral oil gives rise to a sharp loss maximum at 100°K, which does not occur in the pure atactic polymer.