Fracture toughness and crack instability in tough polymers under plane strain conditions

The plane strain fracture toughness and fracture mechanisms of several tough engineering plastics have been studied and compared with poly(methyl methacrylate) (PMMA), a relatively brittle polymer. The tough polymers all are observed to form a multiple craze zone at the crack tip, which is shown to be the primary source of plane strain fracture toughness in these materials. The multiple craze zone is retained during slow crack growth but is metastable, and at a critical stress intensity and associated crack velocity, the system passes through a transition to a greatly accelerated single craze mode of unstable propagation.