Cross-Linked Liquid Crystalline Polyimides with Siloxane Units: Their Morphology and Thermal Diffusivity

Cross-linked liquid crystalline (LC) polyimides with siloxane units have been developed as high thermally conductive materials. The relationship between their thermal diffusivities and film morphologies was investigated. The cross-linking reaction of the LC polyimides was monitored by Fourier transform infrared spectroscopy and differential scanning calorimetry. It was found that the cross-linked LC polyimides successfully maintained their LC structures at room temperature as confirmed by polarized optical microscopy and wide-angle X-ray diffraction (WAXD). The thermal diffusivity of the films in the thickness direction measured by a temperature wave analysis method increased gradually from 0.116 to 0.185 mm 2 s –1 with the increasing extent of the cross-linking. In the detailed WAXD study, the obtained cross-linked LC polyimide films showed that the polymer chains vertically aligned in the thickness direction of the films, and the increase in the extent of the cross-linking expanded the areas of chain alignment. Such a chain alignment plays an important role in the phonon conduction in the thickness direction of the films.