Optical-strain characteristics of anisotropic polymer films fabricated from a liquid crystal diacrylate

The optomechanical characteristics of oriented polymer films made from a photopolymerizable liquid crystal diacrylate (BASF LC242) were examined, with general implications for oriented films of similar materials being used and considered for display-component applications. The birefringence of these uniaxial films before and after polymerization was determined by measuring the retardation between crossed polarizers, (resulting in Δn=0.142±0.002 at 633 nm for the cured polymer films). Optical-strain characteristics were also determined by measuring the transmittance of the films between crossed polarizers at two wavelengths (612 and 633 nm) during the application of a monotonically increasing tensile strain. Under the conservative assumption that Poisson’s ratio is constant for the relatively small strains in our experiment, we develop a strained-waveplate model to detect changes in birefringence directly from the modulation in transmittance with increasing strain. We show that strain applied along the axis of the polymer chains did not substantially affect the birefringence, and strain applied perpendicularly caused only a slight decrease (∼1% decrease for 10% strain). These results highlight the robustness of fully polymerized reactive mesogen optical films to withstand the moderate strains anticipated during manufacturing processes and in-service deformation caused by bending or impact.