CoPt films grown on MgO(001) substrates by molecular-beam epitaxy are expected to develop a very large uniaxial magnetocrystalline anisotropy and a high coercivity when the [001] single variant L10 structure develops along the growth direction. The present study investigates the growth conditions that provide the best structural quality of the films and their related magnetic properties. The quality of the substrate surface, the thickness, and the texture of the Pt buffer layer, the presence or absence of a Cr seed layer, are found to be determinants for the fraction of well-oriented grains in the films, whereas the growth temperature mainly pilots the degree of L10 order η. The uniaxial magnetocrystalline anisotropy energy of the [001] grains (Ku001) is maximum at the stoichiometric composition and shows a linear increase with η. The coercive fields and the magnetic domain size are discussed in relation to the microstructure, the degree of L10 order and the magnetic microscopic constants of the films.
No takes yet. Share an insight, caveat, or question.
Ersen et al. (2003) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: