Self‐organized liquid‐crystalline polyethers obtained by grafting tapered mesogenic groups onto poly(epichlorohydrin): Toward biomimetic ion channels 2

A set of high‐molecular‐weight, new, side‐chain liquid‐crystalline polyethers was obtained by chemical modification of poly(epichlorohydrin) with potassium 3,4,5‐tris[4‐(n‐dodecan‐1‐yloxy)benzyloxy]benzoate. The degree of modification depended on the reaction conditions and ranged from 39 to 58%. The highest value was an apparent modification plateau. NMR characterization indicated no side reactions of any kind (e.g., deshydrohalogenation). All random‐grafted copolymers had hexagonal columnar mesophases with the exception of the least modified copolymer, which had a nematic columnar mesophase. X‐ray diffraction experiments performed on mechanically oriented samples showed that tapered groups were tilted with respect to the column axes.