Pt ∕ ( Ba 0.7 Sr 0.3 ) TiO 3 ( BST ) ∕ YBa 2 Cu 3 O 7 - x ( YBCO ) capacitors were fabricated on (001) LaAlO3 substrates. The leakage current density-electric field characteristics were measured in the temperature range from 20 to 300K. In the electric field region of >0.7MV∕cm for positively biased Pt electrode and >1.4MV∕cm for negatively biased Pt electrode, the leakage current shows space-charge-limited-current behavior from 20 to 250K. Meanwhile a positive temperature coefficient of resistivity (PTCR) in the temperature range from 20 to 150K was observed and attributed to the strong negative temperature dependence of the dielectric constant of BST thin films.