Atomically Thin Tin Monoxide-Based p-Channel Thin-Film Transistor and a Low-Power Complementary Inverter

Atomically thin oxide semiconductors are significantly expected for next-generation cost-effective, energy-efficient electronics. A high-performance p-channel oxide thin-film transistor (TFT) was developed using an atomically thin p-type tin monoxide, SnO channel with a thickness of ∼1 nm, which was grown by a vacuum-free, solvent-free, metal-liquid printing process at low temperatures, as low as 250 °C in an ambient atmosphere. By performing oxygen-vacancy defect termination for the bulk-channel and back-channel surface of the ultrathin SnO channel, the presented p-channel SnO TFT exhibited good device performances with a reasonable TFT mobility of ∼0.47 cm 2 V –1 s –1, a high on/off current ratio of ∼10 6, low off current of <10 –12 A, and a subthreshold swing of ∼2.5 V decade –1, which was improved compared with the conventional p-channel SnO TFTs. We also fabricated metal-liquid printing-based n-channel oxide TFTs such as n-channel SnO 2 and In 2 O 3 -TFTs and developed ultrathin-channel oxide-TFT-based low-power complementary inverter circuits with the developed p-channel SnO TFTs. The full swing of voltage-transfer characteristics with a voltage gain of ∼10 and a power dissipation of <4 nW for p-SnO/n-SnO 2 and ∼120 and <2 nW for p-SnO/n-In 2 O 3 -CMOS inverters were successfully demonstrated.