The effect of the interface/interphase on fiber composite properties

The interfacial region between fibers and matrix in fiber composites governs the transfer of forces between the relatively weak and compliant matrix and the reinforcing fibers. An effective interphase can ensure that the mechanical properties of the composite reflect the high strength and modulus of the fibers. Although composites can be made with the expected strengths and moduli, it is not entirely clear why this is achieved: Tests with critical composites, i.e., those containing very short aligned fibers, do not show the expected stress‐strain behavior. This paper examines the effect of an interphase having a shear modulus that is less than that of the matrix. It is found that to explain the Young's moduli of the short fiber composites, the interphase must have a very low modulus indeed; i.e., a few kPa at most. In addition, the strength results can be accounted for only if we assume that the short lengths of fiber used in the experiments had higher strengths than anticipated. Although agreement between experiments and theory is thus not very good, the small amount of experimental evidence available indicates a need for further systematic experiments on critical (i.e. short aligned fiber) composites before firm conclusions are drawn.