Novel thermotropic esters‐based polymers with broad nematic processing windows

In this study, a new series of semiflexible liquid crystalline (LC) polyesters and poly(ester‐amide)s were synthesized and characterized. Polymers based on 4‐hydroxybenzoic acid (4‐HBA), 6‐hydroxy‐2‐naphthoic acid (HNA), suberic acid (SUA), and sebacic acid (SEA) were modified with hydroquinone (HQ) and different concentrations of 4‐acetamidophenol (AP) to obtain a polyester and two poly(ester‐amide)s, respectively. All polymers were successfully prepared using conventional melt‐condensation techniques. The polymers were characterized by inherent viscosity measurements, SEC, hot‐stage polarizing microscopy, DSC, and TGA. The mechanical behavior was investigated using DMTA and tensile testing. All linear polymers have Tgs in the range of 50–80 °C and melt between 120 and 150 °C. Our polymers display good thermooxidative stabilities (5% wt loss at ∼ 400 °C) and exhibit homogeneous nematic melt behavior over a wide temperature range (ΔN ∼ 250 °C). The liquid crystal phase was lost when high concentrations of nonlinear monomers such as 3‐HBA (>27 mol %) and resorcinol (RC) (>23 mol %) were incorporated. The LC polyester based on 4‐HBA/HNA/HQ/SUA/SEA could easily be processed into good quality films and fibers. The films display good mechanical properties (E′ ∼ 4 GPa) and high toughness, that is, ∼ 15% elongation at break, at room temperature.