Phase Equilibria in the Lead–Magnesium–Niobium–Oxygen System at 1000°C

Phase equilibria in the PbO–MgO–Nb 2 O 5 system have been determined at 1000°C and 1 atm. A solid‐solution range of the cubic pyrochlore phase was observed and the extent of that domain was determined. This solid solution equilibrates with the surrounding ternary and binary compounds to form a series of diphasic areas. The compatibility relations between all phases were determined except for a small domain where at least six lead niobate phases were stable within a very short range of compositions. The formation of pyrochlore impurities during the processing of Pb(Mg 1/3 Nb 2/3 )O 3 perovskite is discussed in relation to the phase diagram.