Fabrication of a Composite Film Optic with High Transmittance in Vis and IR Regions for an Optical System

This is the authors' abstract. We don't add key points for this paper.

In this study, a lightweight composite polyimide film optic with antireflective coating was prepared using an ion-beam-assisted reactive sputtering method. It exhibited high transmittance in visible (87%, 0.5~0.8 μm), short (86%, 1.8~2.7 μm) and middle (78%, 3.3~5.4 μm) wavelength infrared regions. Additionally, it also showed great optical homogeneity (0.006 λ in RMS and 0.034 λ in PV, λ = 632.8 nm) with smooth surfaces (RMS = 0.786 nm). The thermal stability of the polyimide film was also effectively maintained after the antireflective coating. At the same time, by utilizing the hydrophobic properties of coating materials (Ta2O5/SiO2), the antireflective layer acted as an effective water barrier on the film surface to reduce the water absorption.