Study of the Thermal Elimination and Degradation Processes of n-Alkylsulfinyl−PPV and −OC1C10−PPV Precursor Polymers with in Situ Spectroscopic Techniques

We have studied the elimination reaction of n -alkylsulfinyl−PPV and −OC 1 C 10 −PPV precursor polymers toward conjugated materials with in situ FT-IR and UV−vis spectroscopy. The temperature at which the elimination reaction starts in nitrogen flow is as low as 65 and 70 °C, for the PPV and OC 1 C 10 −PPV precursor polymers, respectively. Under vacuum conditions, the elimination temperature shifts even to lower temperatures. After elimination, a certain amount of elimination products, which are set free during the elimination reaction, remain in the OC 1 C 10 −PPV polymer matrix, while in pure PPV, the elimination products are ejected more extremely from the polymer matrix. After completion of the elimination reaction, an absorption maximum of 416 and 490 nm ( T = 150 °C) is obtained for the corresponding PPV and OC 1 C 10 −PPV, respectively. This effective conjugation length decreases again, by degradation of the conjugated system, around 330 °C for the PPV polymer and around 230 °C for the OC 1 C 10 −PPV polymer. From nonisothermal experiments in which the elimination reactions is studied in situ with FT-IR spectroscopy, we are able to determine an experimental activation energy ( E A ) for the conversion reaction, which has a value that is in good agreement with the E A that was obtained by theoretical modeling (104.6 kJ/mol or 25 kcal/mol).