Measurements of Morphology Changes of Fractal Soot Particles using Coating and Denuding Experiments: Implications for Optical Absorption and Atmospheric Lifetime

Mobility-selected fractal and non-fractal soot particles (mobility diameters d m = 135 to 310 nm) were produced at three controlled fuel equivalence ratios (φ = 2.1, 3.5, and 4.5) by an ethylene/oxygen flame. Oleic acid (liquid) and anthracene (solid) coatings were alternately applied to the particles and removed. Simultaneous measurements with an Aerodyne aerosol mass spectrometer and a scanning mobility particle sizer yielded the particle mass, volume, density, composition, dynamic shape factor, fractal dimension, surface area, and the size and number of the primary spherules forming the fractal aggregate. For a given φ, the diameters of the primary spherules are approximately the same, independent of d m (15 nm, 35 nm, and 55 nm for φ = 2.1, 3.5, and 4.5, respectively). As the coating thickness on a particle increases, the dynamic shape factor decreases but d m remains constant until the particle reaches a spherical (for oleic acid) or non-fractal but irregular (for anthracene) shape. Under some conditions, liquid oleic acid coating causes the internal BC framework to rearrange into a more compact configuration. The surface area of fractal particles is up to 2.4 times greater than that of a sphere with the same d m . Using the surface area determinations, the time for a fractal particle to obtain a monolayer of coating material is compared to that of spheres. If it is assumed that the fractal particle is a sphere with the same d m as the fractal particle, the monolayer coating time is underestimated by a factor of up to 1.7.