Effect of gamma irradiation on the interpenetrating networks of gelatin and polyacrylonitrile: Aspect of crosslinking using microhardness and crosslink density measurements

The present article reports the effect of gamma irradiation on the hardness behavior of the interpenetrating polymer networks (IPNs) of gelatin and polyacrylonitrile (PAN). Various compositions of gluteraldehyde‐crosslinked gelatin and N, N′‐methylene bis acrylamide (MBA)‐crosslinked PAN were prepared and investigated for microhardness studies. The pre‐ and post‐irradiated IPNs were characterized for their crosslinking density, determined with swelling ratio measurements. It was found that the crosslinked IPNs get further hardened because of radiational hardening at specific doses in the range from 2 to 250 kGy. The role of acrylonitrile and crosslinker (MBA) in the IPNs, as a consequence of irradiation, has also been explained. A fair consistency has been observed between the microhardness results and crosslinking density measurements.