Oxygen Species Active for Photooxidation of n-Decane over TiO2 Surfaces

Surface-enhanced IR absorption spectroscopy (SEIRAS) was applied to in-situ observation of surface products during the photooxidation of gas-phase n -decane on TiO 2 films coated with an island Au film The bands assignable to C O stretching, O−H stretching, and H−O−H bending were observed with good intensity, indicating the formation of ketone(s) and water on the surface. Ketone as well as water was produced in the dark when a Au/TiO 2 sample was illuminated in advance in O 2 and then exposed to n -decane. This result clearly indicates that oxygen species active for n -decane oxidation remain in the dark after stopping UV irradiation. The formation of ketone and water declined with increasing time lapse of n -decane introduction after illumination, from which the lifetime of the active oxygen species was estimated to be at least 1 min. The active oxygen species formed from O 2 on illuminated Au/TiO 2 were concluded to be O - and O 3 -, judging from the results of ESR and oxygen-isotope tracing measurements so far reported.