Synthesis and characterization of water‐dispersed flame‐retardant polyurethane resin using phosphorus‐containing chain extender

In this research, a flame‐retardant water‐dispersed polyurethane resin was synthesized through incorporating phosphonate groups into the polyurethane structure in the chain‐extension step. A phosphorus‐containing reactive flame‐retardant compound was synthesized for this purpose. First, bis(4‐nitrophenyl)phenyl phosphine oxide was synthesized and then converted to bis(4‐amino phenyl)phenyl phosphine oxide (BAPPO) by reducing its nitro groups into amines. The obtained products were characterized by IR, 1H‐NMR, and 31P‐NMR, and the thermal properties of the polymers were determined by DSC analysis. The BAPPO‐containing polyurethane showed physical properties that were almost similar to those of phosphorus‐free polyurethane and exhibited good flame resistance with a limiting oxygen index value of 27.