Synthesis of a thermoresponsive shell‐crosslinked 3‐layer onion‐like polymer particle with a hyperbranched polyglycerol core

A novel thermoresponsive shell crosslinked three‐layer onion‐like polymer particles were prepared using hyperbranched polyglycerol (PG) as parents compound, the periphery hydroxyl groups of PG were transformed into trithiocarbonates (SC(S)S) first; then, it was used as chain transfer agent to prepare star‐like block copolymer of N‐isopropyl acrylamide (NIPA) and N,N‐dimethylaminoethyl acrylate (DMA) in sequence via reversible addition fragmentation chain transfer (RAFT) process. Thus, a three‐layer polymer, PG[SC(S)S(DMA)b(NIPA)]n, was obtained. The middle layer of poly(DMA) was then crosslinked with 1,8‐diiodoctane, and the resulting onion‐like three‐layer polymer showed a lower critical solution temperature (LCST) in water because of the outer layer of poly(NIPA). The LCST value only slightly depended on the crosslinking degree. Finally, the SC(S)S were transformed into thiols by sequential treating with sodium borohydride and formic acid; thus, the core molecule was chemically detached from the crosslinked shell and a novel shell crosslinked polymer particle was obtained.