Nylon 610/functionalized multiwalled carbon nanotube composite prepared from in‐situ interfacial polymerization

Pristine multiwalled carbon nanotubes (P‐MWNTs) were functionalized with 4‐chlorobenzoic acid via “direct” Friedel‐Crafts acylation in polyphosphoric acid (PPA)/phosphorous pentoxide (P2O5) medium. The resultant 4‐chlorobenzoyl‐functionalized MWNTs (F‐MWNTs) were soluble in chlorinated solvents such as dichloromethane, chloroform, and carbon tetrachloride. A large scale of nylon 610/F‐MWNT composite could be conveniently prepared by in situ interfacial polymerization of 1, 6‐hexamethylenediamine (HMDA) in an aqueous phase, and sebacoyl chloride with F‐MWNTs in an organic phase. Similarly, nylon 610/P‐MWNT composite was also prepared for comparison. The state of F‐MWNTs dispersion in nylon 610 matrix was distinctively better than that of P‐MWNTs, which could be clearly discerned by both naked eye and scanning electron microcopy (SEM). As a result, the tensile strength of nylon 610/F‐MWNT composite was 4.9‐fold higher than that of nylon 610/P‐MWNT composite.