CO 2 ‐Tolerant Ceramic Membrane Driven by Electrical Current for Oxygen Production at Intermediate Temperatures

In this work, an electrochemical oxygen pump ceramic membrane based on Sm 0.2 Ce 0.8 O 1.9 ( SDC ) electrolyte and La 0.6 Sr 0.4 FeO 3−δ ( LSF ) electrode was prepared and characterized by XRD , SEM , and EDX . The area specific resistance of the membranes was measured by impedance spectroscopy. The oxygen electrical permeation behavior of SDC / LSF membrane was investigated under different operating conditions. In consistent with the theoretical prediction from Faraday law, the oxygen flux value observed is closely correlated in quantity with the applied current density. The permeation (or Faraday) efficiency of SDC / LSF membrane could reach above 95% at lower temperatures (600°C–700°C). At 700°C, the oxygen flux through SDC / LSF membrane with 3000 mA/cm 2 current density could reach ~9.97 mL/cm 2 /min. In addition, the prepared SDC / LSF membrane electrical performance was also tested under the presence of CO 2 . It was found that SDC / LSF membrane has excellent structure and permeation stability against CO 2 gas, reflecting its potential applications like oxyfuel technologies and hydrocarbon oxidations.