Inverted Al0.25Ga0.75N/GaN ultraviolet p-i-n photodiodes formed on p-GaN template layer grown by metalorganic vapor phase epitaxy

Inverted Al0.25Ga0.75N/GaN ultraviolet (UV) p-i-n photodiodes (PDs) were grown by selective-area regrowth on p-GaN template. The inverted devices with low-resistivity n-type AlGaN top-contact layers exhibited a typical zero-bias peak responsivity of 66.7 mA/W at 310 nm corresponding to the external quantum efficiency of 26.6%. The typical UV-to-visible (310/400 nm) spectral rejection ratio at zero-bias was over three orders of magnitude. The differential resistance and detectivity were obtained at approximately 6.2×1012 Ω and 3.4×1013 cm Hz1/2 W−1, respectively. Compared with conventional AlGaN/GaN-based UV p-i-n PDs, the proposed device structure can potentially achieve solar-blind AlGaN/GaN-based p-i-n PDs with low-aluminum content or aluminum-free p-contact layer and reduce excessive tensile strain due to the lattice mismatch between AlGaN and GaN layers.