Mesoscopic photosystems for solar light harvesting and conversion: facile and reversible transformation of metal-halide perovskites

Recently, hybrid organic-inorganic metal halide perovskites have gained prominence as potent light harvesters in thin film solid-state photovoltaics. In particular the solar-to-electric power conversion efficiency (PCE) of devices using CH(3)NH(3)PbI(3) as sensitizer has increased from 3 to 20.1% within only a few years. This key material can be prepared by solution processing from PbI(2) and CH(3)NH(3)I in one step or by sequential deposition. In the latter case an electron capturing support such as TiO(2) is first covered with PbI(2), which upon exposure to a CH(3)NH(3)I solution is converted to the perovskite. Here we apply for the first time quartz crystal microbalance (QCMD) measurements in conjunction with X-ray diffraction and scanning electron microscopy to analyse the dynamics of the conversion of PbI(2) to CH(3)NH(3)PbI(3). Employing 200 nm thick PbI(2) films as substrates we discover that the CH(3)NH(3)I insertion in the PbI(2) is reversible, with the extraction into the solvent isopropanol occurring on the same time scale of seconds as the intercalation process. This offers an explanation for the strikingly rapid and facile exchange of halide ions in CH(3)NH(3)PbX(3) by solution processing at room temperature.