Characteristics of Bimodal Polyethylene Prepared via Co‐Immobilization of Chromium and Iron Catalysts on an MgCl2‐Based Support

Bimodal polyethylenes comprising varying proportions of high‐ and low‐molecular‐weight fractions are synthesized in a single polymerization stage, via the co‐immobilization of a chromium and an iron catalyst on an MgCl2/AlEtn(OEt)3−n support. Changes observed in the viscoelastic response of the polymer melt with increasing content of the high‐molecular‐weight fraction indicate effective mixing in the bimodal blend. In flow, chains in the high‐molecular weight fraction tend to orient and stretch under shear. Due to the longer relaxation time of the high‐molecular‐weight component, X‐ray diffraction and scattering reveal that shear‐induced crystallization takes place at temperatures close to the equilibrium melting point of linear polyethylene. The so‐crystallized high‐molecular‐weight component suppresses the nucleation barrier for further crystallization, leading to the formation of a “shish‐kebab” polymer morphology. magnified image