Schottky barrier lowering with the formation of crystalline Er silicide on n-Si upon thermal annealing

The evolution of the Schottky barrier height (SBH) of Er silicide contacts to n-Si is investigated as a function of the annealing temperature. The SBH is found to drop substantially from 0.43 eV for the as-deposited sample to reach 0.28 eV, its lowest value, at 450 °C. By x-ray diffraction, high resolution transmission electron microscopy, and x-ray photoelectron spectroscopy, the decrease in the SBH is shown to be associated with the progressive formation of crystalline ErSi2−x.