Garnet Electrolyte Surface Degradation and Recovery

This is the authors' abstract. We don't add key points for this paper.

Ceramic materials based on the garnet structure Li 7 La 3 Zr 2 O 12 (LLZO) show great promise as lithium-ion conducting electrolytes for solid-state lithium batteries. However, these materials exhibit surface degradation when exposed to air and moisture, which adversely impacts their functioning in operating devices. In this work, we use several depth-profiling and in situ techniques to probe the nature of the surface reactions that occur when aluminum (Al)-substituted LLZO is exposed to air. These experiments show that a proton exchange reaction occurs near the surface of the LLZO and leads to change in its chemistry and structure, concomitant with the formation of Li 2 CO 3 . But these reactions can be readily reversed by heating samples at 250 °C under an inert atmosphere to recover LLZO surface chemistry and structure. Symmetrical cells containing samples treated this way exhibited much lower area specific impedances than those containing air-exposed LLZO without the treatment, confirming the reversal of the degradation process. Our results show a process to rejuvenate LLZO surface, and this opens the possibility of integrating this material in solid-state devices.