Anisotropic Dimensional Swelling of Membranes of Ultrafine Hydrogel Fibers

Summary: Interconnecting fibrous membranes were generated by electrospinning an aqueous mixture of poly(acrylic acid) and poly(vinyl alcohol) at a 3.5 COOH/OH molar ratio. The membranes containing 200 to 500 nm diameter fibers were crosslinked by heat‐induced esterification and behaved like anionic hydrogels, i.e., they swelled significantly more at a pH above 4. The dimensional expansion of these fibrous membranes was far greater in their thickness than in their planar areas. The anisotropic dimensional expansion was associated with the spatial arrangement of fibers, i.e., much smaller inter‐fiber spaces along the thickness direction than in the planar directions. Crosslinking under constraint caused further fiber compaction in the thickness direction, leading to anisotropic and accordion‐like dimensional expansion upon swelling. SEM image of the PAA/PVA membrane (C1) thermally crosslinked under high constraint. magnified image SEM image of the PAA/PVA membrane (C1) thermally crosslinked under high constraint.