Modulation of the absorption coefficient at 13 μm in Ge/SiGe multiple quantum well heterostructures on silicon

We report modulation of the absorption coefficient at 1.3 μm in Ge/SiGe multiple quantum well heterostructures on silicon via the quantum-confined Stark effect. Strain engineering was exploited to increase the direct optical bandgap in the Ge quantum wells. We grew 9 nm-thick Ge quantum wells on a relaxed Si0.22Ge0.78 buffer and a contrast in the absorption coefficient of a factor of greater than 3.2 was achieved in the spectral range 1290-1315 nm.