L1 structure formation in slow-cooled Fe-Au nanoclusters

An ordered L10 structure has been formed in near-stoichiometric Fe-Au alloy nanoparticles. The L10 structure with a = 0.367 nm and c = 0.360 nm was observed in nanoclusters with diameters below 10 nm after slow cooling from 600 °C. The stable L10 structure formed from a parent fcc solid solution phase observed in the as-formed clusters. The fcc phase has a lattice parameter of 0.417 nm, significantly expanded compared to both Au and γ-Fe. The saturation magnetization and coercivity of both fcc and L10 structures were much lower than expected considering Fe dilution effects suggesting competing ferromagnetic and anti-ferromagnetic ordering.