Effect of silver-coated silica nanoparticles on the thermal conductivity of thermally activated acrylic resin

Objective: Thermally activated acrylic resins (RAATs) are widely used in dentures as a base material due to theirgood dimensional stability and biocompatibility. However, their low thermal conductivity is a disadvantage, as itaffects acceptance when using dental prostheses. Thus, the objective of this work was to measure the conductionheat in RAATs with and without incorporation of silica and silver nanoparticles (NP) and rigid reline (RR).Material and Methods: For this, samples were made and divided into 10 groups (n = 6). The first five groupswere 2-mm-thick samples: G1 (RAAT control), G2 (RAAT + RR control), G3 (RAAT and NP + RR), G4 (RAAT+ RR and NP), and G5 (RAAT and RR modified by NP). In the other five groups, 8-mm-thick samples weremade: G6 (RAAT control), G7 (RAAT + RR control), G8 (RAAT and NP + RR), G9 (RAAT + RR and NP), andG10 (RAAT and RR modified by NP). The heat that cross the surface of the specimens was quantified using awireless device. The data were submitted to two-factor ANOVA statistical analysis and Tukey´s test with a 5%significance level. Results: After measuring the temperature variation as a function of time, it can be observedthat there was a statistically significant difference for thermal conduction between the control groups and thosemodified with NP. Conclusion: Thus, it was possible to conclude that the NP improved the heat conduction inRAAT and in the RR because the nanoparticles have a higher thermal conductivity.KEYWORDSThermal conductivity; Acrylic resin; Nanoparticle; Silver.