Extrudate swell from slit and capillary dies: An experimental and theoretical study

A comparative experimental study of extrudate swell from long slit and capillary dies is reported for rheologically characterized polystyrene and polypropylene melts. Generally extrudate swell from a slit is greater than that from a capillary die. At low die wall shear rates it goes to a value of about 1.2 as opposed to about 1.1 found for capillary dies. The onset and character of extrudate distortion have been studied. The experimental results are compared with theories of swell based on unconstrained recovery from Poiseuille flow in these geometries. A detailed analysis of such theories of extrudate swell based on the original work of Tanner has been carried out. The analysis is placed in a more general form which should be valid for a range of die cross‐sections.