Multilayer films using polypropylene/polypropylene grafted with acrylic acid blends and polyamide 6

Blends of polypropylene (PP) with 0 to 100 wt% of polypropylene grafted with acrylic acid (AA-g-PP) were used to promote the adhesion to polyamide 6 (PA 6) in a three-layer coextruded film without using an additional adhesive or tie-layer. The effect of modified polymer content and its molecular weight on interfacial adhesion between PP and PA 6 was determined by T-peel strength measurements. The effect of melt temperature and bonding time on peel strength was determined. Oxygen and water vapor transmission rates of the films were measured. The peel strength of fusion bonded layers of PP/AA-g-PP blends with PA 6 strongly depends on bonding temperature and time, as well as on the molecular weight of the functionalized polymer. The peeled films surfaces were characterized using FTIR-ATR and scanning electron microscopy (SEM). Tensile properties of three-layer films, made up of PA 6 as the central layer and PP/AA-g-PP blends as the two external layers, are improved with increase in the acrylic acid (AA) content in the blend. The formation of an in situ copolymer between AA in the blend and the terminal amine groups of PA 6 was confirmed by the Moalu test.