InGaAs/InAlAs HEMT with a strained InGaP Schottky contact layer

The authors have fabricated an InGaAs/InAlAs HEMT structure with a strained InGaP Schottky contact layer to achieve selective wet gate recess etching and to improve reliability for thermal stress. Strained In/sub 0.75/Ga/sub 0.25/P grown on InAlAs has been revealed to have sufficient Schottky barrier height for use as a gate contact. Threshold voltage standard deviation has been reduced to one fifth that of a conventional InGaAs/InAlAs HEMT, as a result of successful selective recess etching. After thermal treatment at 300 degrees C for 5 min, the drain current and transconductance did not change, while those of the conventional HEMT decreased by more than 10%.>