Nonlinear optical properties of Bi2O3-GeO2 glass at 800 and 532 nm

The nonlinear (NL) optical properties of glassy xBi2O3-(1−x) GeO2 with x = 0.72 and 0.82 were investigated. The experiments were performed with lasers at 800 nm (pulses of 150 fs) and 532 nm (pulses of 80 ps and 250 ns). Using the Kerr gate technique, we observed that the NL response of the samples at 800 nm is faster than 150 fs. NL refraction indices, |n2|≈ 5 × 10−16 cm2/W, and two-photon absorption coefficients, α2, smaller than 0.03 cm/GW, were measured at 800 nm. At 532 nm, we measured the NL transmittance of the samples. From the results obtained, we determined α2 ≈1 cm/GW and excited-state absorption cross-sections of ≈10−22 cm2 due to free-carriers.