Physical properties of unsaturated polyester resin from glycolyzed pet fabrics

Physical properties of unsaturated polyester resins (UPE resins) prepared from glycolyzed poly (ethylene terephthalate) (PET) and PET/cotton blended fabrics were investigated. Initially, PET and PET/cotton blended fabrics were chemically recycled by glycolysis. The depolymerizations were carried out in propylene glycol with the presence of zinc acetate as a catalyst. The reaction time was varied at 4, 6, and 8 h. The glycolyzed products were then esterified using maleic anhydride to obtain UPE resins. The prepared resins were cured using styrene monomer, methyl ethyl ketone peroxide, and cobalt octoate as a crosslinking agent, an initiator and an accelerator, respectively. The cured resin products were tested for their mechanical properties and thermal stability. The results indicated that, among the fabric based resins, one prepared from the 8‐h glycolyzed product possessed the highest mechanical properties those are tensile strength, tensile modulus, flexural strength, impact strength, and hardness. The highest thermal stability was also found in the cured resin prepared from the 8‐h glycolyzed product. The mechanical properties of fabric based resins were slightly lower than those of the bottle based resin.