Synthesis and characterization of novel saponified guar‐graft‐poly(acrylonitrile)/silica nanocomposite materials

The combination of carbohydrates with silicon‐based ceramic materials offers attractive means of production for high performance materials. Present article describes the synthesis of novel nanocomposites out of SiO2 and saponified guar‐graft‐poly(acrylonitrile) (SG). Tetraethoxysilane was used as the precursor for silica and growth of SiO2 phase was allowed concurrently in the presence of SG. The material so obtained was thermally treated at 80°C, 160°C, 500°C, and 900°C to study the effect of thermal curing on its properties. During the curing process, silanol surface groups of silica globules reacted to create the reinforced SiO2‐SG substance. It was observed that at 900°C, the SiO2 phase crystallized out in tetragonal shape (similar to Cristobalite form of silica) in presence of SG. The chemical, structural and textural characteristics of the composites were determined by FTIR, XRD, TGA‐DTA, SEM and BET studies. The materials were also evaluated as efficient Zn2+ metal binder.