Characterization of poly(vinyl alcohol)

Molecular weight distributions, long chain branching frequency, and solution viscosities of samples of commercial poly(vinyl alcohol) (PVA) are reported. The PVA was fully reacetylated to poly(vinyl acetate) (PVAc) for characterizations by size exclusion chromatography using a low angle light scattering detector. The Mark–Houwink constants for PVAc in toluene were determined to be K = 0.106 cm3 g−1 and α = 0.59, at 25°C. Long chain branching frequency in the commercial PVAs studied was small and was little affected by polymer molecular weight. Some 95% or more of the branches in these species were short. Aqueous solutions at 10% (w/v) of PVA were Newtonian. The polymers examined differed in chemical composition, molecular weight distributions, and mean block lengths of vinyl acetate residues. Variations in a single characteristic, like a solution or intrinsic viscosity, cannot be used to deduce structural differences between PVAs.