Palm oil‐based polyester polyol is synthesized by ring opening reaction on epoxidized palm olein by phthalic acid. The reaction is carried out in a solvent free and noncatalyzed condition with the optimal reaction condition at 175°C for 5 h reaction time. The physical state of the product is a clear bright yellowish liquid with low viscosity value of 5700–6700 cP at 25°C and pour point of 15°C. The chemical structure and molecular weight of the polyester polyol were characterized by FTIR, 1H‐NMR, 13C‐NMR, and GPC. The optimal polyol with molecular weight of 36,308 dalton and hydroxyl value of 78.17 mg KOH/g sample was reacted with polymeric 4,4′‐methylene diphenyl diisocyanate (pMDI) at isocyanate index of 1.3 to produce polyurethane adhesive. The lap shear strength of the polyurethane adhesive showed two times higher than the commercial wood adhesives.