Structure and magnetism of epitaxially strained Pd(001) films on Fe(001): Experiment and theory

We present an experimental and theoretical description of the structure and magnetism of epitaxially strained Pd(001) films on Fe(001) and in Fe/Pd/Fe(001) trilayers. The structure is determined by combining reflection high-energy electron diffraction and x-ray diffraction. For Fe/Au(001) bilayers and Fe/Pd/Au(001) trilayers grown by molecular-beam epitaxy on Ag(001), the Fe and Au layers are well represented by their bulk structure, whereas, thin Pd layers have a face-centered tetragonal structure with an in-plane expansion of 4.2% and an out-of-plane contraction of 7.2% (c/a=0.89). Theoretical ab initio studies of the interfacial structure indicate that the structural ground state of the epitaxially strained Pd layer is well described by a fct structure which maintains the bulk Pd atomic volume with small deviations at the interface. For Fe/Pd/Fe trilayers, the interlayer coupling oscillates with a period of 4 monolayers (ML) on a ferromagnetic background that crosses to weak antiferromagnetic coupling for thicknesses >12 ML of Pd. Strong ferromagnetic coupling observed below 5 ML of Pd indicates that 2 ML of Pd at each interface are ferromagnetically ordered. Theoretical studies of Fe₃{Pd}ₙ$ superlattices (where n is the number of Pd atomic layers) determine the polarization of the Pd layer and the interlayer magnetic coupling to depend strongly on the c/a ratio of the Pd layers. Modeling of a Pd layer with a constant-volume fct structure and one monolayer interfacial roughness find that the first 2 ML of the Pd is polarized in close agreement with the experimental results. Polarized neutron reflectivity results on an Fe(5.6 ML)/Pd(7 ML)/Au(20 ML) sample determine the average moment per Fe atom of 2.66±{}0.05μB. Calculations for the same structure show that this value is consistent with the induced Pd polarization.