Electrodeposited Ultrafine NbOx, ZrOx, and TaOx Nanoparticles on Carbon Black Supports for Oxygen Reduction Electrocatalysts in Acidic Media

A remarkable electrocatalytic activity was obtained for the oxygen reduction reaction (ORR) in acidic solutions on ultrafine nano-oxide catalysts based on group IV or V elements. By potentiostatic electrodepostion in nonaqueous solutions at 298 K followed by heat treatment in H 2 gas, highly dispersed fine nanoparticles of NbO x, ZrO x, and TaO x with sizes of less than 5 nm were prepared and deposited on carbon black (CB) loaded electrodes. These oxide nanoparticles showed high catalytic activities with high onset potentials of 0.96 V RHE (NbO x ), 1.02 V RHE (ZrO x ), and 0.93 V RHE (TaO x ) for the ORR. Owing to the high chemical stability of group IV and V oxides, the catalysts were very stable during the ORR in acidic solutions. Surface characterization and chemical identification were performed using scanning transmission electron microscopy (STEM), energy dispersive X-ray spectroscopy (EDS), and X-ray photoelectron spectroscopy (XPS). All results clearly indicate the formation of nano-oxide electrocatalysts that show an outstanding ORR performance, whereas the bulk oxides are not active because of the absence of electronic conductivity. The present work demonstrates potential candidates for highly stable, non-noble-metal cathode catalysts for polymer electrolyte fuel cells (PEFCs), where the catalysts are exposed to highly acidic and oxidizing conditions.