An immobilization technique for semisoft colloidal crystals, which are ordered arrays of polymer-brush-afforded hybrid particles synthesized by surface-initiated living radical polymerization (SI-LRP), is reported. Silica particles were first grafted with well-defined block copolymers of poly(methyl methacrylate-co-hydroxyethyl methacrylate)-b-poly(methyl methacrylate), P(MMA-co-HEMA)-b-PMMA by SI-LRP, which gave a graft density as high as 0.7 chains/nm(2). The HEMA units reacted with 2-isocyanatoethyl methacrylate to introduce vinyl groups at the outer layer of the polymer-brush shell. The modified hybrid particles formed a colloidal crystal in a solution containing a small amount of free polymers with vinyl groups. The colloidal crystal was photoirradiated in the presence of a photoradical initiator to immobilize it through a cross-linking reaction among the vinyl groups. The structural analyses of the colloidal crystals before and after the photoirradiation were carried out by confocal laser scanning microscopy; the results showed that the periodic structures of the crystals were maintained after immobilization.
No takes yet. Share an insight, caveat, or question.
Huang et al. (2014) studied this question.
Synapse has enriched 5 closely related papers on similar clinical questions. Consider them for comparative context: