Tailoring adsorption induced phase transitions in the pillared-layer type metal–organic framework DUT-8(Ni)

This is the authors' abstract. We don't add key points for this paper.

C NMR, PXRD, SEM, IR and Raman spectroscopy shows that the crystallite size is a crucial factor, determining the differing characteristics such as "gate pressure" and adsorption capacity in the guest-responsive switching behaviour of DUT-8. Crystallites smaller than 500 nm in size retain the open form after removal of the guest molecules resulting in typical "Type Ia" isotherm, whereas crystallites larger than 1 μm transform into the "closed pore" form and therefore can show a characteristic "gate opening" behaviour during gas adsorption. The particle size distribution of DUT-8(Ni) can be tailored by changing the synthesis conditions and consequently the slope of the isotherm at the "gating step" is affected. The in depth analysis of synthesis conditions and switching behaviour is an important step towards a better understanding of the fundamental principles responsible for guest responsive porosity switching in the solid state.