CO Oxidation Mechanisms on CoOx-Pt Thin Films

The reaction of CO and O 2 with submonolayer and multilayer CoO x films on Pt(111), to produce CO 2, was investigated at room temperature in the mTorr pressure regime. Using operando ambient pressure X-ray photoelectron spectroscopy and high pressure scanning tunneling microscopy, as well as density functional theory calculations, we found that the presence of oxygen vacancies in partially oxidized CoO x films significantly enhances the CO oxidation activity to form CO 2 upon exposure to mTorr pressures of CO at room temperature. In contrast, CoO films without O-vacancies are much less active for CO 2 formation at RT, and CO only adsorbed in the form of carbonate species that are stable up to 260 °C. On submonolayer CoO x islands, the carbonates form preferentially at island edges, deactivating the edge sites for CO 2 formation, even while the reaction proceeds inside the islands. These results provide a detailed understanding of CO oxidation pathways on systems where noble metals such as Pt interact with reducible oxides.