Reactive compatibilization of nylon copolymer/EPDM blends: experimental aspects and their comparison with theory

In situ reactive compatibilization was first time applied to a low melting nylon (nylon 6 and 66 copolymer) and EPDM blend system. The effects of in situ compatibilization and concentration of compatibilizer on the morphology and mechanical properties of nylon/EPDM blends have been investigated. The influence of EPM‐g‐MA on the phase morphology was examined by the scanning electron microscopy (SEM) after preferential extraction of the minor phase. The SEM micrographs were quantitatively analyzed for domain size measurements. The compatibilizer concentrations used were 0, 1, 2.5, 5, and 10 wt%. The graft copolymer (nylon‐g‐EPM) formed at the interface showed relatively high emulsifying activity. A maximum phase size reduction was observed when 2.5 wt% of compatibilizer was added to the blend system. This was followed by a leveling‐off at higher loadings indicating interfacial saturation. The conformation of the compatibilizer at the interface was deduced based on the area occupied by the compatibilizer at the blend interface. The experimental compatibilization results were compared with theoretical predictions of Noolandi and Hong. It was concluded that the molecular state of compatibilizer at interface changes with concentration. The in situ compatibilized blends showed considerable improvement in mechanical properties. Measurement of tensile properties shows increased elongation as well as enhanced modulus and strength up on compatibilization. At higher concentrations of compatibilizer, a leveling‐off of the tensile properties was observed. A good correlation has been observed between the mechanical properties and morphological parameters.