Effect of 30 Mev Li 3+ ion and 8 MeV electron irradiation on n-channel MOSFETs

The effect of 30 v MeV Li 3+ ion and 8 v MeV electron irradiation on the threshold voltage ( V TH ), the voltage shift due to interface trapped charge ( j V Nit ), the voltage shift due to oxide trapped charge ( j V Not ), the density of interface trapped charge ( j N it ), the density of oxide trapped charge ( j N ot ) and the drain saturation current ( I D v Sat ) were studied as a function of fluence. Considerable increase in j N it and j N ot , and decrease in V TH and I D v Sat were observed in both types of irradiation. The observed difference in the properties of Li 3+ ion and electron irradiated MOSFETs are interpreted on the basis of energy loss process associated with the type of radiation. The study showed that the 30 v MeV Li 3+ ion irradiation produce more damage when compared to the 8 v MeV electron irradiation because of the higher electronic energy loss value. High temperature annealing studies showed that trapped charge generated during ion and electron irradiation was annealed out at 500 v °C.