High solubility, low‐dielectric constant, and optical transparency of novel polyimides derived from 3,3′,5,5′‐tetramethyl‐4,4′‐diaminodiphenyl‐4″‐isopropyltoluene

A series of novel polyimides (PIs) (3a–d) were prepared from 3,3′,5,5′‐tetramethyl‐4,4′‐diaminodiphenyl‐4″‐isopropyltoluene (1) with four aromatic dianhydrides via a one‐step high temperature polycondensation procedure. The obtained PIs showed excellent solubility, with most of them dissoluble at a concentration of 10 wt % in amide polar solvents and chlorinated solvents. Their films were nearly colorless and exhibited high‐optical transparency, with the UV cutoff wavelength in the range of 328–353 nm and the transparency at 450 nm >80%. They also showed low‐dielectric constant (2.49–2.94 at 1 MHz) and low‐water absorptions (0.44–0.65%). Moreover, these PIs possessed high‐glass transition temperatures (Tg) beyond 327 °C and excellent thermal stability with 10% weight loss temperatures in the range of 530–555 °C in nitrogen atmosphere. In comparison with some fluorinated poly(ether imide)s derived from the trifluoromethyl‐substituted bis(ether amine)s, the resultant PIs 3a–d showed better solubility, lower cutoff wavelength, and higher Tg.