Effect of solvents on the cryogenic dynamic mechanical properties of polystyrene

Young's modulus and mechanical damping of 15 organic liquids in polystyrene have been measured from 4°K to 250°K. The concentration was generally in the range from 10 to 15%, but the polystyrene–toluene system was investigated over the range from 0 to 16%. Some liquids cause the 40°K damping peak of polystyrene to disappear, other liquids do not. Seven of the liquids which cause the disappearance of the 40°K peak give rise to new large damping peaks at the temperature expected for the secondary glass transition temperatures of the liquids, that is, at 0.77 Tg of the liquids. Some of the liquids produced large unexplained damping peaks at temperatures above the expected glass transition temperatures Tg of the liquids. It is suggested that the γ peak in polystyrene is caused by styrene monomer.